Özet
In this study, we produced Aluminum oxide (Al2O3) reinforced carbon fiber and glass fiber reinforced polymer (CFRP, GFRP) composites and investigated mechanical and tribological properties. Al2O3 was dispersed in epoxy resin using a mechanical stirrer. The composites are produced via the hand lay-up method and dried at room temperature for 48 hours. The properties of composites were determined via Archimedes’ method, flexural, impact, hardness and wear tests. The highest flexural strength and hardness were found at 946.3 MPa and 48.7 HBA for 3 wt.% Al2O3 reinforced CFRP, respectively. The highest impact strength was observed at 187.4 kJ/m2 for an un-reinforced GFRP composite. The lowest Coefficient of Friction (COF) and wear depth was found 3 wt.% Al2O3 reinforced GFRP composites.
Açıklama
Anahtar Kelimeler
Composite and Hybrid Materials, Kompozit ve Hibrit Malzemeler
Kaynak
Hittite Journal of Science and Engineering
WoS Q Değeri
Scopus Q Değeri
Cilt
10
Sayı
4