Ti3C2Tx MXene/reduced graphene oxide/cellulose nanocrystal-coated cotton fabric electrodes for supercapacitor applications

Abstract

Textile-based electrodes are the most important components of wearable and portable supercapacitors. Ti3C2Tx MXene and reduced graphene oxide (rGO) have a great potential for the fabrication of high-performance textile supercapacitor electrodes. In this work, rGO was synthesized with the presence of cellulose nanocrystal (CNC) and Ti3C2Tx/rGO/CNC dispersions with different rGO/CNC contents were prepared. The plain-woven cotton fabrics were coated by homogenous Ti3C2Tx and Ti3C2Tx/rGO/CNC dispersions (5% wt., 15% wt., 30% wt. and 50% wt. rGO/CNC content) and characterized by X-ray Diffraction, Fourier Transform Infrared spectroscopy and Scanning Electron Microscopy techniques. The electrochemical characterization techniques showed that Ti3C2Tx/rGO/CNC loaded fabric electrodes up to 15 wt.% rGO/CNC content exhibited a high specific capacitance of 501.1 F g(-1) at a current density of 0.3 A g(-1) with low internal electrode resistance, and a good electrochemical stability. The results also showed that MXene/rGO/CNC based high-performance textile supercapacitor electrodes can be prepared by simple drop-casting method.