Wood Property Improvement of Siberian Pine by Combination of Boric Acid Impregnation and In-Situ Polymerization of ?-Caprolactone

Basit Öğe Kaydı
dc.contributor.authorErmeydan, Mahmut Ali
dc.contributor.authorTomak, Eylem Dizman
dc.contributor.authorKartal, Zeynep Nur
dc.date.accessioned2026-02-12T21:01:21Z
dc.date.available2026-02-12T21:01:21Z
dc.date.issued2019
dc.departmentBursa Teknik Üniversitesi
dc.description.abstractWood is an excellent engineering material with its light weight and high mechanical properties. However, it is susceptible to biodegradation due to its hygroscopic nature and chemical composition that limits both its indoor and outdoor usage. Boron compounds which are known as eco-friendly wood preservatives have limited utility at outdoor conditions since they are easily leached out from wood by water. The aim of this study is to prevent boron leaching by creating a polymer network that encapsulates boron compound inside the wood cell walls, thus decay resistance, dimensional stability and water repellence are improved. In the study, Siberian pine samples were impregnated with 1% boric acid in DMF(N,N-Dimethylformamide) and further ?-caprolactone monomer (1% SnOct2 as initiator) mixture for further in-situ polymerization were carried out in the oven at 150°C for 3 hours. Prior to decay testing, leaching test was conducted in order to evaluate any loss in effectiveness in decay resistance against to C. puteana and C. versicolor attack due to possibility of boron leaching from wood. The results showed that leached samples had lower weight loss than unleached samples after C. puteana attack, however, the weight loss by C. versicolor attack increased in leached samples. Decay resistance of treated samples was found to be 7-99% in comparison with references. Boric acid and polymer combination increased dimensional stability (25% ASE), and water repellence (15%) of wood compared to references without deformation. This method showed that curing may be an alternative for wood modification with in-situ polycaprolactone polymerization in order to use hazardous solvent media for polymerization.
dc.identifier.endpage161
dc.identifier.issn1302-0900
dc.identifier.issn2147-9429
dc.identifier.issue1
dc.identifier.startpage157
dc.identifier.trdizinid315533
dc.identifier.urihttps://hdl.handle.net/20.500.12885/6522
dc.identifier.volume22
dc.indekslendigikaynakTR-Dizin
dc.language.isoen
dc.relation.ispartofPoliteknik Dergisi
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_TR-Dizin_20260212
dc.subjectBiyoloji
dc.subjectNanobilim ve Nanoteknoloji
dc.subjectMantar Bilimi
dc.subjectMalzeme Bilimleri
dc.subjectKâğıt ve Ahşap
dc.subjectBiyoloji Çeşitliliğinin Korunması
dc.titleWood Property Improvement of Siberian Pine by Combination of Boric Acid Impregnation and In-Situ Polymerization of ?-Caprolactone