Long-Term Leaching Effect on Decay Resistance of Wood-Plastic Composites Treated with Boron Compounds

Basit Öğe Kaydı
dc.authorid0000-0001-8654-0005en_US
dc.contributor.authorCavdar, Ayfer Donmez
dc.contributor.authorDizman Tomak, Eylem
dc.contributor.authorMengeloglu, Fatih
dc.date.accessioned2021-03-20T20:13:21Z
dc.date.available2021-03-20T20:13:21Z
dc.date.issued2018
dc.departmentBTÜ, Orman Fakültesi, Orman Endüstri Mühendisliği Bölümüen_US
dc.description.abstractIn this study, water absorption, thickness swelling and decay resistance of thermoplastic composites treated with three types of boron compounds was investigated. Spruce wood flour was treated with boric acid (BA), borax (BX) and mixture of BA-BX, and then was reinforced at two loading rate (20 and 40 wt%) in polymer matrix. Decay test of the composites was performed using with a brown rot fungus Coniophora puteana and a white rot fungus Trametes versicolor both for leached and unleached samples. The morphologic evaluations of decayed samples were done by scanning electron microscopy. Composites containing higher wood flour loading resulted in increased water absorption, thickness swelling, weight loss and moisture content. Fungal decay susceptibility of WPCs was influenced by leaching test for 60 days. Boron compound treated composites showed higher weight loss and moisture content than controls in decay test. All tested performance parameters were considerably increased in BX containing composites.en_US
dc.identifier.doi10.1007/s10924-017-0992-7en_US
dc.identifier.endpage764en_US
dc.identifier.issn1566-2543
dc.identifier.issn1572-8900
dc.identifier.issue2en_US
dc.identifier.scopusqualityQ1en_US
dc.identifier.startpage756en_US
dc.identifier.urihttp://doi.org/10.1007/s10924-017-0992-7
dc.identifier.urihttps://hdl.handle.net/20.500.12885/850
dc.identifier.volume26en_US
dc.identifier.wosWOS:000425964600032en_US
dc.identifier.wosqualityQ2en_US
dc.indekslendigikaynakWeb of Scienceen_US
dc.indekslendigikaynakScopusen_US
dc.institutionauthorDizman Tomak, Eylem
dc.language.isoenen_US
dc.publisherSpringer/Plenum Publishersen_US
dc.relation.ispartofJournal Of Polymers And The Environmenten_US
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectCompositesen_US
dc.subjectDecayen_US
dc.subjectLeachingen_US
dc.subjectPolymeren_US
dc.subjectBoron compoundsen_US
dc.subjectMoisture contenten_US
dc.subjectSwellingen_US
dc.titleLong-Term Leaching Effect on Decay Resistance of Wood-Plastic Composites Treated with Boron Compoundsen_US
dc.typeArticleen_US

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Orman Endüstri Mühendisliği Bölümü Yayın Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu