Effect of water curing temperature on compressive strength development and water absorption capacity of mortar mixtures

Basit Öğe Kaydı
dc.contributor.authorAghabaglou, Ali Mardanı
dc.contributor.authorÖzen, Süleyman
dc.contributor.authorAltun, Muhammet Gökhan
dc.contributor.authorFaqırı, Zia Ahmad
dc.date.accessioned2026-02-08T15:05:07Z
dc.date.available2026-02-08T15:05:07Z
dc.date.issued2020
dc.departmentBursa Teknik Üniversitesi
dc.description.abstractIn this study, the effect of different curing temperature processes on the 1, 3, 7 and 28-day compressive strength and 28-day water absorption ratios of mortar mixtures were investigated. All mortar mixtures were prepared according to ASTM C109. The water/cement ratio, sand/binder ratio and flow values of mortar mixture were kept constant as 0.485, 2.75 and 25±2 cm, respectively. Polycarboxylate ether-based high range water reducing admixture was used for providing desired flow value. All mortar mixtures were cured at fresh state in a curing room under the same conditions (Temperature of 20?C and Relative humanity (RH) of 95%) during 24 hours from casting. Then, specimens were subjected to 6 different water-curing conditions. According to test results, the 3-day compressive strength of mixtures cured in water having a temperature of 40ºC was higher than that of mixtures cured at 20ºC in water. At early ages, the high curing temperature negatively affected the 7 and 28-day compressive strength of mixtures. Specimens cured in water at 20ºC and 40ºC had the highest and lowest 28-day compressive strengths, respectively. Different curing conditions had no significant effect on the 28-day water absorption ratios of mortar mixtures.
dc.identifier.endpage148
dc.identifier.issn1304-7191
dc.identifier.issn1304-7205
dc.identifier.issue1
dc.identifier.startpage135
dc.identifier.urihttps://hdl.handle.net/20.500.12885/4446
dc.identifier.volume38
dc.language.isoen
dc.publisherYıldız Teknik Üniversitesi
dc.relation.ispartofSigma Mu?hendislik ve Fen Bilimleri Dergisi
dc.relation.ispartofSigma Journal of Engineering and Natural Sciences
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_DergiPark_20260207
dc.subjectEngineering
dc.subjectMühendislik
dc.titleEffect of water curing temperature on compressive strength development and water absorption capacity of mortar mixtures