Isıl İşleme Tabi Tutulmuş Ahşap Malzemelerin Boyutsal Stabilitesi

Basit Öğe Kaydı
dc.contributor.authorEşener, Vahit
dc.contributor.authorTomak, Eylem Dizman
dc.date.accessioned2026-02-08T15:02:53Z
dc.date.available2026-02-08T15:02:53Z
dc.date.issued2025
dc.departmentBursa Teknik Üniversitesi
dc.description.abstractAhşabın boyutsal kararlılığı ve nem içeriği, onun nihai kullanımını etkileyen önemli fiziksel özelliklerdendir. Bu çalışmada, meşe (Quercus spp.), sarı kavak (Dalbergia decipularis), ayous (Triplochiton scleroxylon K. Schum), iroko (Milicia excelsa), dişbudak (Fraxinus spp.) ve çam (Pinus sylvestris) türlerine ait keresteler endüstriyel bir ısıl işlem tesisinde 212°C’de termal modifikasyona tabi tutulmuştur. Termal modifiyeli ve termal modifiyesiz (kontrol) kerestelerden 20x20x30 mm boyutlarında örnekler kesilmiştir. Her grup için 10 adet örnek kullanılmıştır. Tam kuru ağırlık ve boyutları belirlenen örnekler, daha sonra suyun içerisinde 5 gün boyunca bekletilmiş ve süre sonunda tekrar tam kuru ağırlık ve boyutları alınmıştır. Bu döngü 2 kez tekrarlanmıştır. Deneyde örneklerin su alma oranı (%), su itici etkinliği (%), hacimsel genişleme katsayısı (%) ve boyutsal stabilitesi (%) hesaplanmıştır. Sonuç olarak, termal modifiyeli örneklerde kontrollerine kıyasla en az su alma oranı meşe ve ayous odununda görülmüştür. Su itici etkinlik açısından, çam ve sarı kavak örneklerde ısıl işlemin etkisi diğer odun türlerine kıyasla daha düşük tespit edilmiştir. Hacimsel genişleme katsayısı ise, ısıl işlemli dişbudak, çam, sarı kavak ve nispeten meşede, kontrollerine kıyasla önemli ölçüde düşük bulunmuştur. Test edilen 6 tür arasında en düşük boyutsal stabilite iroko odununda tespit edilmiştir.
dc.description.abstractThe moisture content and dimensional stability of wood are crucial physical properties that influence its end-use performance. In this study, oak (Quercus spp.), tulip (Dalbergia decipularis), ayous (Triplochiton scleroxylon K. Schum), iroko (Milicia excelsa), ash (Fraxinus spp.) and pine (Pinus sylvestris) timbers were subjected to thermal modification at 212°C in an industrial heat treatment factory. Samples with dimensions of 20x20x30 mm were cut from both thermally modified and unmodified (control) timbers. Ten samples were used for each sample group. After measuring the oven-dry weight and dimensions of the specimens initially determined, then they were immersed in water for 5 days, and the oven-dry weight and dimensions were measured again at the end of this period. This cycle was repeated 2 times. In the experiment, the water uptake rate (%), water-repellent efficiency (%), volumetric swelling coefficient (%), and dimensional stability (%) of the specimens were calculated. As a result, the lowest water uptake rate among the thermally modified samples compared to their controls was observed in oak and ayous wood. In terms of water-repellent efficiency, the effect of heat treatment was found to be lower in pine and tulip samples compared to other wood species. The volumetric swelling coefficient was found to be significantly lower in heat-treated ash, pine, tulip, and oak compared to their controls. Among the 6 species tested, the lowest dimensional stability was found in iroko wood.
dc.identifier.doi10.59751/agacorman.1670718
dc.identifier.endpage75
dc.identifier.issn2757-5349
dc.identifier.issn2757-5349
dc.identifier.issue1
dc.identifier.startpage69
dc.identifier.urihttps://doi.org/10.59751/agacorman.1670718
dc.identifier.urihttps://hdl.handle.net/20.500.12885/3706
dc.identifier.volume6
dc.language.isotr
dc.publisherBursa Technical University
dc.relation.ispartofAğaç ve Orman
dc.relation.ispartofTree and Forest
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_DergiPark_20260207
dc.subjectWood Protection Technology
dc.subjectOdun Koruma Teknolojisi
dc.titleIsıl İşleme Tabi Tutulmuş Ahşap Malzemelerin Boyutsal Stabilitesi
dc.title.alternativeDimensional Stability of Heat-Treated Wood Materials
dc.typeArticle

Dosyalar

Koleksiyon

Ağaç ve Orman Koleksiyonu