Investigation of casting quality change of A356 by duration in liquid state

Basit Öğe Kaydı
dc.authorid0000-0001-9150-3292en_US
dc.contributor.authorUludağ, Muhammet
dc.contributor.authorGurtaran, M.
dc.contributor.authorDispinar, D.
dc.date.accessioned2021-03-20T20:26:57Z
dc.date.available2021-03-20T20:26:57Z
dc.date.issued2019
dc.departmentBTÜ, Mühendislik ve Doğa Bilimleri Fakültesi, Metalurji ve Malzeme Mühendisliği Bölümüen_US
dc.description.abstractThis study aims to investigate how casting quality change in aluminum melt during the holding period in liquid state. 10 kg of ingot was melted in a SiC crucible by using an electrical furnace. A sample was taken every five minutes from 0 to 55 min after the alloy was melted. Reduced pressure test (RPT) samples were collected to be solidified under 80 mbar. All samples were sectioned into two parts vertically, and one of them was prepared for metallographic examination. Surface of the samples was subjected to image analysis by using via image analysis software. Bifilm index and bifilm area were analyzed in detail. As a result, it can be concluded that first 30 min of liquid metal is important, because casting quality tends to get worse after 30 min. © The Minerals, Metals & Materials Society 2019.en_US
dc.identifier.doi10.1007/978-3-030-06034-3_16en_US
dc.identifier.endpage166en_US
dc.identifier.issn2367-1181
dc.identifier.scopus2-s2.0-85064066644en_US
dc.identifier.scopusqualityQ3en_US
dc.identifier.startpage159en_US
dc.identifier.urihttp://doi.org/10.1007/978-3-030-06034-3_16
dc.identifier.urihttps://hdl.handle.net/20.500.12885/1362
dc.indekslendigikaynakScopusen_US
dc.institutionauthorUludağ, Muhammet
dc.language.isoenen_US
dc.publisherSpringer International Publishingen_US
dc.relation.ispartofMinerals, Metals and Materials Seriesen_US
dc.relation.publicationcategoryKitap Bölümü - Uluslararasıen_US
dc.rightsinfo:eu-repo/semantics/closedAccessen_US
dc.subjectA356 alloyen_US
dc.subjectBifilmsen_US
dc.subjectCasting qualityen_US
dc.subjectHolding timeen_US
dc.titleInvestigation of casting quality change of A356 by duration in liquid stateen_US
dc.typeBook Chapteren_US