    Effect of precipitation on mechanical and wear properties of ultrafine-grained Cu-Cr-Zr alloy
    (Elsevier Science Sa, 2014) Purcek, G.; Yanar, H.; Saray, Onur; Kraman, I.; Maier, H. J.
    The effect of an ultrafine-grained (UFG) microstructure and subsequent aging treatment on the mechanical and wear behavior of a Cu-Cr-Zr alloy was investigated. The results indicate that the precipitates dispersed within the UFG matrix significantly enhance the strain hardening, resulting in improvement of hardness, strength and wear resistance of the alloy, without notably sacrificing the elongation to failure and electrical conductivity, due to the combined effect of grain refinement and precipitation. The wear behavior of Cu-Cr-Zr alloy was found to be strongly dependent on its strength and hardness. The minimum weight loss (or the highest wear resistance) was obtained when the sample was processed by equal channel angular extrusion (ECAE) through an additional aging treatment, as this resulted in ultra-high strength and hardness. The wear results also indicate that the wear behavior of Cu-Cr-Zr alloy in all processing conditions is consistent with the Archard approach. Complex wear mechanisms such as adhesive, oxidative and abrasive wear, and delamination were found to be operative in the differently processed Cu-Cr-Zr alloys. It is to be concluded that the use of a two-step process, the first resulting in an UFG microstructure and a subsequent aging treatment provides a simple and effective procedure for extraordinary increase in strength, hardness and wear resistance of Cu-Cr-Zr alloys without modification of the chemical composition. (C) 2014 Elsevier B.V. All rights reserved.
  • Küçük Resim Yok
    Öğe
    Room temperature superplasticity in fine/ultrafine-grained Zn-Al alloys with different phase compositions
    (Trans Tech Publications Ltd, 2018) Demirtas, M.; Yanar, H.; Saray, Onur; Purcek, G.
    Three Zn-Al alloys, namely Zn-22Al, Zn-5Al and Zn-0.3Al, were subjected to equal-channel angular pressing (ECAP), and the effect of ECAP on their microstructure and room temperature (RT) superplastic behavior were investigated in detail referring to previous studies reported by the authors of the current study. ECAP remarkably refined the microstructures of three alloys as compared to their pre-processed conditions. While the lowest grain size was achieved in Zn-22Al alloy as 200 nm, the grain sizes of Zn-5Al and Zn-0.3Al alloys were ~540 nm and 2 µm, respectively, after ECAP. After the formation of fine/ultrafine-grained (F/UFG) microstructures, all Zn-Al alloys exhibited superplastic behavior at RT and high strain rates. The maximum superplastic elongations were 400%, 520% and 1000% for Zn-22Al, Zn-5Al and Zn-0.3Al alloys, respectively. It is interesting to point out that the highest RT superplastic elongation was obtained in Zn-0.3Al alloy with the largest grain size, while Zn-22Al alloy having the lowest grain size showed the minimum superplastic elongation. This paradox was attributed to the different phase compositions of these alloys. The formation of Al-rich ?/? phase boundaries, where grain boundary sliding is minimum comparing to Zn-rich ?/? and ?/? phase boundaries of Zn-Al alloys, is the lowest level in Zn-0.3Al alloy among all the alloys. Therefore, it can be concluded that if it is desired to achieve high superplastic elongation in Zn-Al alloys at RT, keeping Al content at a possibly minimum level seems to be the most suitable way. © 2018 Trans Tech Publications, Switzerland