Kalemtaş, AyşeTopates, GulsumAydin, M. Turkay AytekinOzey, Nigar2021-03-202021-03-2020202187-0764http://doi.org/10.1080/21870764.2019.1710017https://hdl.handle.net/20.500.12885/524Highly porous SiC ceramics containing borax decahydrate were produced by a starch consolidation method in which corn starch was used as a shaping and pore-forming additive. Four different compositions were prepared with different SiC:borax decahydrate ratios and corn starch content. Mixtures with a solid ratio of 55 wt.% were cast in non-porous molds and heated at 80 degrees C for shaping. The starch consolidation technique enabled the shaping of SiC ceramics with different forms and sizes. Simultaneous thermogravimetry and differential thermal analysis of the SiC-borax decahydrate mixture showed that melting took place at below 600 degrees C, as a result of which sintering was carried out at the relatively low temperature, of 600 degrees C in the air using borax decahydrate as a sintering additive. Phase analysis showed that oxidation of SiC did not take place, since no cristobalite phase was detected. Density measurement and mercury porosimetry studies showed that highly porous (70-89% porosity) SiC ceramics with pore size values ranging from 14 to 18 mu m were produced. SEM microstructures of each composition revealed that a strong neck had been formed between the SiC particles in spite of the low sintering temperature.eninfo:eu-repo/semantics/openAccessStarch consolidationPorous SiCTG-DTASintering under atmospheric conditionsLow-temperature sinteringArticle10.1080/21870764.2019.171001781106115WOS:000506274000001Q1Q2